Flame retardant fabric, Fire resistant fabrics

中文版 ENGLISH

·Multifunctional tarpaulin



Tarpaulin for airplane	Tarpaulin for tank

·The main traits of the new tarpaulin of airplane (in army)
    a) The base fabric is made of polyester canvas, it just be dyed and managed to waterproof, no coated, no dipped with mucus. The tarpaulin well in water-vapour penetrative, just like the base fabric.
    b) Well in waterproof, the hydrostatic pressure can meet 470mm water column.
    c) High in rupture strength and tear strength, meet the standards.
  d) Widely used as tarpaulin in airplane、 tank、 folk-car、 provide disaster relief and material’s cover.

·The main traits of the new tank tarpaulin
    a) A great improvement in flame retardant, the smoldering time almost reduced to 0, and it can cut down the second fire in smoldering greatly.
   b) The coating film with no protrusion, avoiding the damage from the needle and hard, can improve the lifetime of the tarpaulin
   c) The new tarpaulin have the function of vitriol resistant, and it can meet the standards of GB12012-89《The acid work clothing and the test method of it’s capability》
    d) A great improvement in oil-proof, it can meet the 7th grade (130 marks), the standard is 4th grade (80 marks) actually.
    e) The rupture strength and tear strength are better than standards.

·The test report of flame retardant infrared resistant acid resistant oil-proof waterproof endure to hydrostatical) pressure in polyester tarpaulin

NO.	Test Items				Standards	Results	Conclusion
1	Dry weight， g/㎡				≤510	500	eligibility
2	Breadth， cm				150±2	150±2	eligibility
3	Rupture strength， N		Warp		≥1900	2150	eligibility
			Weft		≥1300	1408
4	Tear strength， N		Warp		≥70	250	eligibility
			Weft		≥40	141
5	Capability of flame retardant			Continuous combustion， S	＜3	1.5	eligibility
				smouldering， S	＜5	1.0
				Damaged length， cm	＜10	8.5
6	hydrostatical pressure， water column (cm)				≥45	＞80	eligibility
7	Waterproof， grade				4	4	eligibility
8	Oil-proof， mark				80	＞130	eligibility
9	Bear to vitriol （the time of dip in vitriol)， minutes				≥30	＞30	eligibility
10	Vapour transfer rate， g/㎡.24h				≥1800	1900	eligibility
11	Color				Green	Green	eligibility
12	color fastness to dry rub， grade				≥4	4	eligibility
13	Working temperature ，℃				-43～+50	-43～+50	eligibility
14	Bear to aging				no brittle fracture in -43℃；no sticky in 100℃180 hours	no brittle fracture in -43℃；no sticky in 100℃	eligibility
15	Spectrum reflectivity，% （700～1500nm）				10～80	73	eligibility
Test standards		GB8965-1998《flame retardant garment》 GB12799-91《the requirement of safety and sanitation in oil-proof and waterproof garment》 GB12012-89《acid resistant garment》 GB/T3923.1-1997《The stretch capability on fabrics and textile part one: the mensuration of mightiness of rupture and elongation percentage of rupture strip method》 GB/T3917.3-1997《the tear capability on fabrics and textile part three: the mensuration of tear capability on trapezoidal method》 GB/T12704-91《the mensuration of vapour transfer on textile vapour transfer method》 GB/T4744-1997《the mensuration of anti-permeate on textile hydrostatical pressure method》
Conclusion		The sample meet the standards demanded according to the test.